High Cr White Iron Castings Chute Liners Hardness More Than HRC57

Wuxi Orient Anti-wear Engineering Co.,Ltd.

High Cr White Iron Castings Chute Liners Hardness More Than HRC57

  • 1
  • 2

Brand Name : Chen's Liner

Model Number : DF1019

Certification : ISO9001:2008

Place of Origin : Jiangsu,China(Mainland)

MOQ : 2tons

Price : USD 2,000-4,000 per ton

Payment Terms : L/C,T/T

Supply Ability : 25000 Ton/Tons per year.

Delivery Time : It depends on quantity to be ordered.

Packaging Details : Packed by strong steel pallets.

Material : High Cr Cast Iron

Dimension : As per drawing

Application : Mining Industry

MOQ : 2tons

Heat Treatment Process : Quenching and Tempering

Package : Steel Pallet

Contact Now

High Cr White Iron Castings Chute Liners Hardness More Than HRC57

Summarization

High Cr white iron material possess a combination of superior abrasion resistance and a reasonable

degree of toughness. The high Cr castings have longer service life than the other material,such as

high Mn steel and Cr-Mo alloy steel.And now it is widely used in the working condition of high wear and low impact,such as dry grinding process,coal mills,cement mills due to its excellent performance.

Specification

Model Number DF1019
Material High Cr Cast Iron
Hardness ≥HRC57
Dimension As per drawing
Process Sand Casting
Impact Value ≥AK 10J
Inspection

Dimensional Inspection

Chemical Composition Inspection

Hardness Inspection

UT Test
Application Coal Mill,Cement Mill,Mining Industry etc.
MOQ 2Tons
Delivery Time Depends on the quantity to be ordered.
Port Shanghai
Package Steel Pallets
Payment Terms T/T,L/C

Product Photo

High Cr White Iron Castings Chute Liners Hardness More Than HRC57

High Cr White Iron Castings Chute Liners Hardness More Than HRC57

Technical Parameters

Item High Cr White Iron High Cr Alloy Steel High Mn Steel Ni-hard Cast Iron
C 2.4-3.2 1.1-2.2 0.9-1.3 2.4-3.6
Si 0.6-1.2 0.6-1.2 ≤0.8 ≤0.8
Mn 0.5-1.0 0.5-1.0 11.0-18.0 ≤2.0
Cr 12.0-30.0 11.0-30.0 1.5-2.5 1.5-10
S ≤0.04 ≤0.04 ≤0.04 ≤0.15
P ≤0.06 ≤0.06 ≤0.06 ≤0.15
Mo 0.1-3.0 0.1-3.0 ≤1.0 ≤0.1
Cu 0.1-1.0 0.1-1.0 - -
Ni 0-0.3 0-0.3 - 3.3-10
Re - - - -
Equivalent
Specification
GB/T8263-1999
AS2027 Cr27
AS2027 CrMo 15/3
AS2027 CrMo 20/2/1
ASTM A532 Class Ⅲ Type A 25%Cr
ASTM A532 Class Ⅱ Type B 15%Cr-Mo
BS 4844 3E
DIN1695
NFA32401
GB/T5680-1998
DL/T 681-1999
JIS G 5153-1999
ASTM A128
DIN GX120Mn12
AFNORZ120Mn12
GB/T8263-1999
AS2027/Ni-Cr1-550
AS2027/Ni-Cr2-500
AS2027/Ni-Cr4-500
AS2027/Ni-Cr4-600
AS2027/Ni-Cr4-630
ASTM A532 1-A,B,C,D
ASTM A532 2-A,B,C,D,E
ASTM A532 3-A
Material Type Martensite Matrix Austenitic Mn Steel -
Hardness HRC≥56 HB≤300 HRC≥56
Impact Value AK≥4J AK≥80J -

Company Introduction

High Cr White Iron Castings Chute Liners Hardness More Than HRC57

Inspection Facilities

High Cr White Iron Castings Chute Liners Hardness More Than HRC57

High Cr White Iron Castings Chute Liners Hardness More Than HRC57


Quality High Cr White Iron Castings Chute Liners Hardness More Than HRC57 for sale

High Cr White Iron Castings Chute Liners Hardness More Than HRC57 Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Wuxi Orient Anti-wear Engineering Co.,Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)